Compositions for dissolving metal sulfates

ABSTRACT

A scale dissolver composition and method for using the composition is provided. Broadly, the dissolver compositions are formed by adding a base such as ammonium hydroxide to a mixture comprising a salt of a chelating agent, a carbonate, and a component selected from the group consisting of organophosphorus compounds, carboxylic acids, and mixtures thereof. The preferred organophosphorus compound is aminotristmethylidine diphosphonic acid while the preferred chelating agent salt is EDTA tetrasodium salt. In use, the dissolver composition is preferably heated to a temperature of from about 100-170° F. and then contacted with the target scale. The compositions are particularly useful for removing barium sulfate and calcium sulfate scales from gas and oil well and pipeline equipment in an efficient and cost-effective manner.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention is broadly concerned with compositions fordissolving scales (and particularly metal sulfate scales) and methods ofusing the same. More particularly, the scale dissolver compositions ofthe invention comprise an aqueous dispersion which includes a salt of achelating agent, a carbonate, a base, and a component selected from thegroup consisting of organophosphorus compounds, carboxylic acids, andmixtures thereof. In use, the dissolver compositions are contacted withthe target scale, preferably after first heating the composition. Thecompositions are particularly useful for removing calcium sulfate andbarium sulfate scales from gas and oil well equipment, boilers, andpipes.

2. Description of the Prior Art

Many waters contain alkaline earth metal cations such as barium,strontium, calcium, and magnesium, and anions such as sulfate,bicarbonate, carbonate, phosphate, and fluoride. When combinations ofthese anions and cations are present in concentrations which exceed thesolubility product of the various species which may potentially beformed, precipitates form until the respective solubility products areno longer exceeded. For example, when concentrations of barium andsulfate ions exceed the solubility product of barium sulfate, a solidphase of barium sulfate will form as a precipitate. The formation ofsolubility products are affected by several factors including pH,temperature, pressure, and the presence of a seed crystal. When thesesolubility products form, they precipitate on the surface ofwater-carrying or water-containing systems and form adherent deposits orscales which cause serious problems. For example, during gas and oilproduction, scale plugging of surface and subsurface equipment, tubings,and perforations often lead to severe productivity declines anddifficult operating conditions. Of the sulfate scales, barium sulfate isparticularly troublesome because of its extreme insolubility.

Previous methods have been attempted to dissolve sulfate scales. Forexample, U.S. Pat. No. 5,183,112 to Paul et al. discloses a method fordissolving calcium sulfate wherein a scale-removing solvent comprising achelating agent and the anions of a monocarboxylic acid, oxalates, orthiosulfates is injected into a well followed by sparging of the solventwith air or an inert gas. However, sparging with air or gas is adifficult and messy process, and is quite messy.

Prior art attempts at dissolving barium sulfate include utilizingboiling sulfuric acid. This is impractical and dangerous for dissolvingdownhole barium sulfate. Another method for removing barium sulfate isto fracture (“frac”) it with extremely high pressure. However, thisprocess is quite costly in that it requires special equipment and extramanpower, and results in lengthy well downtimes. Another prior artprocess for removing barium sulfate is to perforate the scale. This isalso not very effective. In some instances, when scales present too muchof a problem, the well is simply abandoned and a new well is drilledwhen scales present too much of a problem. Obviously, this is a verycostly solution.

SUMMARY OF THE INVENTION

The present invention overcomes the prior art problems by providing aneffective, inexpensive scale dissolver that is particularly effective atdissolving sulfate scales such as alkaline earth metal sulfate scales.Furthermore, the dissolver compositions of the invention are relativelyeasy to use.

The scale dissolver compositions comprise an aqueous dispersion whichincludes a salt of a chelating agent, a carbonate, a base, and acomponent selected from the group consisting of organophosphoruscompounds, carboxylic acids, and mixtures thereof. The chelating agentis preferably a salt of EDTA (or mixture of EDTA salts) such as EDTAtetrasodium salt (sold under the tradename VERSENE 100), trisodium EDTA,or the edetates. The chelating agent should be present in thecomposition at a level of from about 10-70% by weight, and preferablyfrom about 30-50% by weight, based upon the total weight of thecomposition taken as 100% by weight.

Suitable carbonates for use in the instant invention include all alkalimetal carbonates and bicarbonates, with sodium bicarbonate beingparticularly preferred. Preferably, the carbonate is present in thecomposition at a level of from about 0.1-10% by weight, and morepreferably from about 2-6% by weight, based upon the total weight of thecomposition taken as 100% by weight.

While most bases are suitable for use with the dissolver compositions,it is preferred that the base comprise an OH group. Preferred basesinclude ammonium hydroxide (preferably at a solution concentration offrom about 28-30%) and pure NH₃ gas. The base should be present in thecomposition at a level of from about 0.1-10% by weight, and morepreferably from about 2-6% by weight, based upon the total weight of thecomposition taken as 100% by weight.

When the scale to be dissolved comprises barium sulfate, it is preferredthat an organophosphorus compound, such as an organophosphonic acid, beutilized in the dissolver compositions of the invention. A particularlypreferred organophosphonic acid is aminotrismethylidine diphosphonicacid sold under the tradenames PHOS-2, DEQUEST 2000, and UNIHIB 305. Theorganophosphorus compound is preferably present in the composition at alevel of from about 0.1-10% by weight, and more preferably from about2-6% by weight, based upon the total weight of the composition taken as100% by weight.

When the scale to be dissolved comprises calcium sulfate, it ispreferred that a carboxylic acid (preferably one having from 2-6 carbonatoms) be included in the dissolver composition. A particularlypreferred carboxylic acid for use in the instant invention ishydroxyacetic acid. The carboxylic acid should be present in thecomposition at a level of from about 0.1-10% by weight, and morepreferably from about 2-6% by weight, based upon the total weight of thecomposition taken as 100% by weight.

The compositions of the invention are formed by preparing a mixturecomprising the chelating agent salt, the carbonate, and the componentselected from the group consisting of organophosphorus compounds,carboxylic acids, and mixtures thereof. The desired base is then addedto this mixture approximately 10-15 minutes after the mixture is formed.It is important to wait this amount of time in order to prevent thecarbonate from falling out of solution. The final mixture should have apH of from about 7-8.5, preferably from about 7.2-8.0, and morepreferably about 7.5. If necessary, the pH should be adjusted to thisrange by utilizing small quantities of the base, the carbonate, and/ororganophosphorus compound as necessary to reach the desired pH.

In use, the dissolver compositions arc simply contacted with the scaleto be dissolved or removed. The quantity of dissolver compositionrequired is generally from about 0.5-5 gallons of composition, andpreferably from about 1-3 gallons of composition, per 2.65 lbs of scale.It is preferred, that the composition be heated to a temperature of fromabout 100-170° F., and more preferably from about 120-150° F., prior tothe contacting step in order to more efficiently remove/dissolve thescale. Advantageously, after about 0.5-3 hours at least about 75% of thescale, and preferably at least about 100% of the scale, is dissolved orremoved from the contaminated surface.

Those skilled in the art will appreciate that the instant compositionsare particularly useful for removing downhole scale in oil and gas wellsthus providing an effective alternative to the prior art methods. Whentreating oil and gas wells or pipelines with the dissolver compositions,the composition is simply injected into the well or pipeline so that itcontacts the target scale as described above. Again, it is preferredthat the composition first be heated to the above-described temperaturesprior to injection. After injection, hot oil or hot water is preferablyflushed into the well or through the pipeline.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS EXAMPLES

The following examples set forth preferred methods in accordance withthe invention. It is to be understood, however, that these examples areprovided by way of illustration and nothing therein should be taken as alimitation upon the overall scope of the invention.

Example 1 Compositions for Dissolving Barium Sulfate

The following formulation was used to form a barium sulfate-dissolvingcomposition:

TABLE 1 % By Compound Quantity Weight^(a) Dequest 2000(aminotristmethylidine 3.5 ml 3% diphosphonic acid) Versene 100(ethylenediaminetetraacetic acid 50 ml 42.3% tetrasodium salt) Sodiumbicarbonate 5 g 3.35% Ammonium hydroxide 5 ml 2.9% Distilled water 70 ml45.6% ^(a) Based upon total weight of all components taken as 100% byweight.

The Dequest 2000 and Versene 100 were mixed together with sodiumbicarbonate being added to the resulting mixture. The sodium bicarbonatewas allowed to react with the Dequest 2000/Versene 100 mixture forseveral minutes to form a solution. Ammonium hydroxide (28%) was addedto the solution followed by the distilled water. The pH of the finalsolution was then adjusted with Dequest 2000 until it was in the rangeof 7-8.5. Approximately 25 ml of the solution was placed in a beaker andheated to about 160° F. in a hot water bath. A piece of barium sulfatewas added to the heated solution. The barium sulfate was completelydissolved within 15 minutes.

The above procedure was repeated five times with a different compoundused in place of the Dequest 2000 each time and with the remainingcompounds being as described above. The following compounds were used inplace of Dequest 2000 during the five repetitions: HEDP; Unihib 106;Unihib 905; Phosphorous acid; and Briquest ADPA-60AW. In each of theruns, approximately the same size piece of barium sulfate was use. Table2 sets forth the results for each of the five repetitions. Based uponthese results, the solution which included Dequest 2000 was the mosteffective, with the respective solutions containing HEDP or BriquestADPA-60AW being the next most effective. The solutions which includedUnihib 905 or phosphorous acid were the least effective.

TABLE 2 Compound in Solution Observations HEDP Solution dissolved theBaSO₄ slowly. After 30 minutes about half of the BaSO₄ remained. Afterone hour the majority of the BaSO₄ had been dissolved. Unihib 106(1-hydroxyethylene- BaSO₄ dissolution was initially rapid but fadedquickly. After 15 minutes, a detectable amount 1,1-diphosphonic acid) ofthe BaSO₄ had been dissolved, but after 30 minutes there was almost nochange in the amount of BaSO₄ remaining. After 1 hour, the BaSO₄ hadbroken apart and only very small particles remained. Unihib 905 After 30minutes and after 60 minutes, only a small amount of BaSO₄ haddissolved. After 1½ (diethylenetriaminepenta(methyl- hours, the BaSO₄pieces had broken apart but a significant amount of BaSO₄ remained.After 2 enephosphonic acid) hours, BaSO₄ pieces still remained.Phosphorous acid Sample exhibited bubbling action but BaSO₄ did notsignificantly dissolve in 30 minutes. After 1 hour the BaSO₄ pieces wereslightly smaller and bubbling less. After 2 hours, no bubbling actionremained. The beaker was shaken and some of the remaining BaSO₄ brokeapart. Briquest ADPA 60-AW (1- A small amount of the BaSO₄ was goneafter 15 minutes. An further small amount washydroxyethylidene)bis-phosphonic dissolved after 30 minutes. After 50minutes the BaSO₄ broke apart, and after 1 hour there were acid onlyvery small pieces remaining. Dequest 2000 Solution dissolved the BaSO₄fairly quickly. After 15 minutes the sample was dissolved.

Example 2 Compositions for Dissolving Calcium Sulfate

The following formulation was used to form a calcium sulfate-dissolvingcomposition:

TABLE 2 % By Compound Quantity Weight^(a) Hydroxyacetic acid 3.5 ml 2.9%Versene 100 (ethylenediaminetetraacetic acid 50 ml 42.3% tetrasodiumsalt) Sodium bicarbonate 5 g 3.35% Ammonium hydroxide 5 ml 2.9%Distilled water 70 ml 45.6% ^(a)Based upon total weight of allcomponents taken as 100% by weight.

Hydroxyacetic acid and Versene 100 were mixed together with sodiumbicarbonate being added to the resulting mixture. The sodium bicarbonatewas allowed to react with the hydroxyacetic acid/Versene 100 mixture forseveral minutes to form a solution. Ammonium hydroxide (28%) was addedto the solution followed by the distilled water. The pH of the finalsolution was then adjusted with hydroxyacetic acid until it was in therange of 7-8.5. Approximately 25 ml of the solution was placed in abeaker and heated to about 160° F. in a hot water bath. A piece ofcalcium sulfate was added to the heated solution. The calcium sulfatewas completely dissolved within 15 minutes.

We claim:
 1. A composition for dissolving metal sulfates comprising anaqueous dispersion including: a component selected from the groupconsisting of (1) an organophosphorus compound which is a salt of achelating agent, (2) other organophosphorus compounds, (3) hydroxyaceticacid, and (4) mixtures thereof; sodium bicarbonate; a base; and a saltof a chelating agent when said component does not include (1) of saidgroup.
 2. The composition of claim 1, wherein said component is anorganophosphorus compound.
 3. The composition of claim 2, wherein saidcomponent is an organophosphonic acid.
 4. The composition of claim 3,wherein said component is aminotrismethylidine diphosphonic acid.
 5. Thecomposition of claim 2, wherein said organophosphorus compound ispresent in said composition at a level of from about 0.1-10% based uponthe total weight of the composition taken as 100% by weight.
 6. Thecomposition of claim 1, wherein said chelating agent salt is a salt ofEDTA.
 7. The composition of claim 6, wherein said salt is EDTAtetrasodium salt.
 8. The composition of claim 1, wherein said chelatingagent salt is present in said composition at a level of from about10-70% by weight, based upon the total weight of the composition takenas 100% by weight.
 9. The composition of claim 1, wherein said sodiumbicarbonate is present in said composition at a level of from about0.1-10% by weight, based upon the total weight of the composition takenas 100% by weight.
 10. The composition of claim 1, wherein said basecomprises an OH group.
 11. The composition of claim 10, wherein saidbase is ammonium hydroxide.
 12. The composition of claim 1, wherein saidbase is present in said composition at a level of form about 0.1-10% byweight, based upon the total weight of the composition taken as 100 byweight.
 13. The dispersion of claim 1, wherein the pH of the aqueousdispersion is from about 7-8.5.
 14. A composition for dissolving metalsulfates comprising an aqueous dispersion including: a componentselected from the group consisting of (1) an organophosphorus compoundwhich is a salt of a chelating agent, (2) other organophosphoruscompounds, (3) carboxylic acids, and (4) mixtures thereof; sodiumbicarbonate; a base; and a salt of a chelating agent when said componentdoes not include (1) of said group, said composition being capable ofdissolving at least about 75% by weight of said metal sulfates afterabout 0.5-3 hours.
 15. A method of forming a composition comprising anaqueous dispersion for dissolving metal sulfates, said method comprisingthe steps of: from a mixture comprising: from about 0.1-10% by weightsodium bicarbonate, the percentage by weight being based upon the totalweight of the composition taken as 100% by weight; a component selectedfrom the group consisting of (1) an organophosphorus compound which is asalt of a chelating agent, (2) other organophosphorus compounds, (3)carboxylic acids, and (4) mixtures thereof; and when said component doesnot include (1) of said group, a salt of a chelating agent; and adding aquantity of a base to said mixture to form the dispersion, saidcomposition being capable of dissolving at least 75% by weight of saidmetal sulfates after about 0.5-3 hours.
 16. A method of forming acomposition comprising an aqueous dispersion for dissolving metalsulfates, said method comprising the steps of: forming a mixturecomprising an alkali metal carbonate or bicarbonate, a componentselected from the group consisting of (1) an organophosphorus compoundwhich is a salt of a chelating agent, (2) other organophosphoruscompounds, (3) carboxylic acids, and (4) mixtures thereof, and when saidcomponent does not include (1) of said group, a salt of a chelatingagent; and about 10-15 minutes after said forming step, adding aquantity of a base to said mixture to form the dispersion, saidcomposition being capable of dissolving at least 75% by weight of saidmetal sulfates after about 0.5-3 hours.